Abstract
This article is devoted to the following issues: calculating the values of temperatures obtained by simulating welding heating and the subsequent implementation of the welding process at the given mode parameters made it possible to obtain a welded joint of the rotor with an improved initial structure and increased mechanical properties, hydrogen resistance and durability by up to 10–15%; simulating welding heating in the areas of fusion, the overheating and normalization of the HAZ and the formation of austenite grains; specified welding heating creates the conditions for the formation of new products of austenite decomposition in the form of sorbitol in the area of the incomplete recrystallization of the HAZ. In air and gaseous hydrogen, the destruction of the combined joints took place on the weld metal, as well as on the fusion areas, the overheating and the incomplete recrystallization of the HAZ of 20H3NMFA steel as the base metal. Structural materials have a relatively low strength and high fracture toughness in air. This is manifested in a significant reduction in the elongation (δ), the area (ψ) and critical stress intensity factor (KIc) of welded joints and the endurance limit of cylindrical smooth rotor steel specimens, which were cut from transverse templates. Welded joints in the whole range of load amplitudes are sensitive to the action of hydrogen.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.