Abstract

Silica (SiO2) can be extracted from rice husks and has biodegradable properties. However, the rice husk extraction process using the sol-gel technique generates low-purity silica, making them non-compliant as a filler material on the rubber finished goods industry. This study aimed to improve the characteristics of silica particles extracted from rice husks using the leaching-pyrolysis technique compared to the sol-gel technique. Silica was extracted from rice husks using 1.0 N sodium hydroxide and hydrochloric acid solvent (with concentrations of 0.4 N, 1.0 N, and 2.0 N). The pyrolysis was then conducted at 600 °C for 6 hours. The results showed that the leaching-pyrolysis technique was more effective than the sol-gel technique in improving silica particle characteristics. X-ray fluorescence analysis showed that the SiO2 content increased from 91.00 % to 96.82 %. Likewise, the percentage of amorphous by X-ray diffraction analysis and specific surface area by the Brunauer Emmett-Teller method also increased, namely from 48.20 % to 53.97 % and from 96.486 m2/g to 240.427 m2/g, respectively. Therefore, silica from rice husks with these characteristics is applicable as a filler material that is environmentally friendly and renewable.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.