Abstract
Photorefractive properties of Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording sensitivity are observed and explained. The decrease in Li vacancies is suggested to be the main contributor to the increase in the photoconductivity and subsequently to the induction of the improvement of recording sensitivity. The saturation diffraction efficiency is measured up to 80.2%, and simultaneously the recording sensitivity of 0.91 cm/J is achieved to in the Hf:Fe:LiNbO3 crystal grown from the melt with the [Li]/[Nb] ratio of 1.20, which is significantly enhanced as compared with those of the Hf:Fe:LiNbO3 crystal with the [Li]/[Nb] ratio of 0.94 in melt under the same experimental conditions. Experimental results definitely show that increasing the [Li]/[Nb] ratio in crystal is an effective method for Hf:Fe:LiNbO3 crystal to improve its photorefractive properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.