Platinum nanoparticles (Pt NPs) have been selectively anchored by photodeposition on titanium oxide (TiO2) matrix which is formed by hydrolysis of titanium isopropoxide on cup–stacked carbon nanotubes (CSCNT) in isopropanol, producing the composite Pt catalyst useful for oxygen reduction reaction (ORR) in acidic media, i.e., Pt NPs/TiO2/CSCNT. Using scanning transmission electron microscopy (STEM) with a high–angle annular–dark–field (HAADF) detector it has been clarified that Pt NPs are sunk into the TiO2 moieties and have the unique polyhedral shape surrounded mainly by the Pt (1 1 1) and Pt (1 0 0) facets. X–ray photoelectron spectroscopy (XPS) allowed us to confirm changes in electronic properties of both Pt NPs and TiO2 support, induced by the so-called strong metal–support interactions (SMSI) and the significantly increased ORR activity was attained in 0.1M HClO4, compared with the Pt NPs deposited on CB (Vulcan carbon) and CSCNT. The surface structure of the Pt NPs was characterized by transmission electron microscopy (TEM), indicating the improved durability of the Pt NPs deposited on the TiO2/CSCNT, i.e., the only slight increase in the particle size after the durability test (typically 2000 times’ potential cycling at 10mVs−1 in the potential ranges of 0.05 to 1.1V and 1.0 to 1.5V vs. RHE in 0.1M HClO4). The results obtained demonstrate that the anchoring of Pt NPs on the TiO2 support material deposited on CSCNT is an effective way to enhance the ORR activity of Pt NPs by the SMSI as well as to prohibit Pt NPs from aggregating, i.e., the degradation of the ORR activity of Pt NPs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.