Abstract
Carbon nanocoils (CNCs) synthesized using thermal pyrolysis chemical vapor deposition on 304 stainless steel wire substrates were used as the cathodes of field emission lamps (FELs). The effects of the growth temperature on the FE performances were studied, and we observed that uniform and dense CNCs that are suitable for use as FE cathodes can be synthesized at 600°C. We also found that a nitrogen doping post-treatment can significantly improve the FE efficiency of the CNCs. When doped at 200°C with a nitrogen flow rate of 500sccm for 30min, the nitrogen content of the CNC surface could reach 4.9wt.%. ESCA analysis indicates that the doped nitrogen atoms formed CNx bonding and increased the sp2 clusters in the CNCs. The turn-on voltage was reduced from 2.1V/μm to 1.4V/μm, and the β value increased considerably from 2465 to 3241 after N-doping post-treatment. The bulb-type FELs using our N-doped CNC cathodes showed a good luminous efficiency as high as 75lm/W at 8kV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.