Abstract
It is critical for carbon fiber/epoxy (CF/EP) composites to have a high resistance to atomic oxygen (AO) erosion when they are utilized in a low earth orbit (LEO) environment. Herein, we proposed a simple method whereby a silane coupling agent (SCA) was applied onto the carbon fiber surface to fabricate CF/EP composites with both improved interfacial shear strength (IFSS) and AO erosion resistance. The SCA was first hydrolyzed, then reacted with the hydroxyl groups on the pretreated CF surface, and finally formed a continuous uniform layer of siloxane oligomers. Atomic force microscopy images exhibited relatively smooth surfaces for SCA-treated CFs after AO erosion, when compared to the rough surface for bare CFs. It was found that the IFSS and AO erosion resistance were improved for SCA-coated CFs and CF/EP composite interface since a silica (SiO2) layer was formed upon exposure to AO as confirmed by XPS results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.