Abstract
Three-layer films were prepared with polyethylene (PE) and poly(ethylene terephthalate) (PET) films as the outer layers and a film of high-density polyethylene (HDPE)/ethylene-methyl acrylate-glycidyl methacrylate (E-MA-GMA) terpolymer blend as the inner layer using compression molding. E-MA-GMA, an elastomer containing an epoxy functional group, was used as the adhesion promoting agent in the multilayer films. The effects of processing temperature, pressure application time and elastomer concentration on adhesion were investigated. The adhesion strength between PE and PET films increased with increasing bonding temperature, bonding time and elastomer concentration. From contact angle measurements, it was observed that the work of adhesion between the polymers increased with increasing amount of elastomer. Improved adhesion between PET and HDPE with 30% elastomer films was confirmed by SEM analyses of the film layers. Using FT-IR analysis of PE/HDPE-30% elastomer/PET delaminated film, the decrease in peak intensity of the epoxy groups tends to indicate reaction of epoxy functionality with functional groups in PET.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.