Abstract
Abstract The Tc and oxygen content of TlBa2CaCu2Oy have been investigated by quenching experiments, in which the heat-treated samples were dropped into liquid nitrogen. The oxygen loss, v, of TlBa2CaCu2Oyo − v was determined by thermogravimetry in a nitrogen atmosphere using an oxygen-annealed specimen of TlBa2CaCu2Oyo and also by measurements of the weight differences before and after quenching. Tc increased from 80 K of the oxygen-annealed specimen up to about 110 K with increasing oxygen loss up to v = 0.035 by annealing at 500°C in a nitrogen atmosphere. Judging from the high Tc above 110 K achieved by a small oxygen loss about v = 0.035, the as-sintered oxygen-annealed TlBa2CaCu2Oyo specimen was in the over-doping state and probably has an oxygen vacancy of 7 − yo0.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.