Abstract
For use in high-magnetic-field coil-based applications, the critical current density (Jc) of REBa2Cu3Oy (REBCO, where RE = rare earth) coated conductors must be isotropically improved, with respect to the direction of the magnetic field; these improvements must be realized at the operating conditions of these applications. In this study, improvement of the Jc for various applied directions of magnetic field was achieved by controlling the morphology of the BaHfO3 (BHO) nano-rods in a SmBCO film. We fabricated the 3.0 vol. % BHO-doped SmBCO film at a low growth temperature of 720 °C, by using a seed layer technique (Ts = 720 °C film). The low-temperature growth resulted in a morphological change in the BHO nano-rods. In fact, a high number density of (3.1 ± 0.1) × 103 μm−2 of small (diameter: 4 ± 1 nm), discontinuous nano-rods that grew in various directions, was obtained. In Jc measurements, the Jc of the Ts = 720 °C film in all directions of the applied magnetic field was higher than that of the non-doped SmBCO film. The Jcmin (6.4 MA/cm2) of the former was more than 6 times higher than that (1.0 MA/cm2) of the latter at 40 K, under 3 T. The aforementioned results indicated that the discontinuous BHO nano-rods, which occurred with a high number density, exerted a 3D-like flux pinning at the measurement conditions considered. Moreover, at 4.2 K and under 17 T, a flux pinning force density of 1.6 TN/m3 was realized; this value was comparable to the highest value recorded, to date.
Highlights
Improvement in Jc performance below liquid nitrogen temperature for SmBa2Cu3Oy superconducting films with BaHfO3 nano-rods controlled by low-temperature growth
For use in high-magnetic-field coil-based applications, the critical current density (Jc) of REBa2Cu3Oy (REBCO, where RE = rare earth) coated conductors must be isotropically improved, with respect to the direction of the magnetic field; these improvements must be realized at the operating conditions of these applications
The aforementioned results indicated that the discontinuous BHO nano-rods, which occurred with a high number density, exerted a 3D-like flux pinning at the measurement conditions considered
Summary
Improvement in Jc performance below liquid nitrogen temperature for SmBa2Cu3Oy superconducting films with BaHfO3 nano-rods controlled by low-temperature growth. Improvement of the Jc for various applied directions of magnetic field was achieved by controlling the morphology of the BaHfO3 (BHO) nano-rods in a SmBCO film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.