Abstract
AbstractThe wettability of polyurethane (PU) was altered using ultraviolet ozone (UVO) treatment. The effect of UVO treatment on PU surface chemistry was investigated with various experiments. The direct measurement of sessile drops was employed to quantify the static contact angle of different wetting liquids on homogeneous PU films with various UVO treatment times. The contact angle of DI water droplets was decreased to 17.2° from 70.04° after 5 min UVO treatment. The surface free energy of PU films was 51.46 mN m−1 before treatment and was increased to 71.5 mN m−1 after being fully treated. X‐ray photoelectron spectroscopy (XPS) analysis shows a significant amount of polar functional species (CO and CO bonding) were formed on the PU surface by UVO treatment. atomic force microscopy (AFM) characterization shows the PU surface morphology was different before and after UVO treatment. The effect of water washing on UVO treated surface was also investigated. An aging effect study indicates the UVO modification can sustain the improved wettability with limited hydrophobic recovery, where the DI water contact angle remains constant at around 22° after the UVO treatment. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.