Abstract

We investigated the electrical and optical performance and reliability of 278 nm deep ultraviolet (DUV) AlGaN-based flip-chip light-emitting diodes (FCLEDs) fabricated with ITO/Al and reference Ni/Au contacts. The DUV FCLEDs with the Ni/Au and ITO/Al contacts yielded forward voltages of 6.52 and 6.65 V at 50 A cm−2 and light output of 6.36 and 10.06 mW at 50 A cm−2, respectively. The ITO/Al-based FCLEDs produced higher Wall plug efficiency (WPE) (3.04% at 50 A cm−2) than the Ni/Au-based samples (1.96%). The ITO/Al-based FCLEDs revealed 55% higher WPE at 50 A cm−2 than the Ni/Au-based sample. For both of the samples, the output power decreased with increasing operation time at 100 A cm−2. For example, after 2000 h, the Ni/Au and ITO/Al-based FCLEDs showed a reduction in the output power by 37% and 22%, respectively. Despite the good output characteristics, the ITO/Al contact-based FCLEDs exhibited higher forward bias voltages than the Ni/Au-based sample. Based on the energy dispersive X-ray spectroscopy (EDS) depth profiles, high-angle annular dark field (HAADF), and electron energy loss spectroscopy (EELS) results, reason for the increase in the forward voltage of ITO/Al-based FCLEDs is described and discussed.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.