Abstract
Zigzag TiO2 nanostructures were fabricated using oblique angle deposition technique. The field emission gun-scanning electron microscope (FEG-SEM) image shows that the TiO2 zigzag nanostructures were ~500 nm in length. Averagely two times enhanced UV-Vis absorption was recorded for zigzag structure compared to perpendicular TiO2 nanowires. The main band transition was observed at ~3.4 eV. The zigzag TiO2 exhibited high turn on voltage (+11 V) than that of nanowire (+2 V) detector under dark which were reduced to +0.2 V and +1.0 V under white light illumination, respectively. A maximum ~6 fold photo-responsivity was observed for the zigzag TiO2 compared with nanowire device at + 1.0 V applied potential. The maximum photo-responsivity of 0.36 A/W at 370 nm was measured for the zigzag TiO2 detector. The TiO2 zigzag detector showed slow response with rise time of 10.2 s and fall time of 10.3 s respectively. The UV (370 nm) to visible (450 nm) wavelength rejection ratio of photo-responsivity was recorded ~4 times for the detector.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.