Abstract
The ceramic (1-x)BiFe0.985Sc0.015O3-xBaZr0.2Ti0.8O3 + 1mol% MnO2 (x = 0.20, 0.25, 0.30, 0.35) (BFS-xBZT) was synthesized using the traditional ceramic sintering method. The components of the ceramic were determined by constructing a morphotropic phase boundary (MPB) which consists of rhombohedral (R) and tetragonal (T) phases (0.24≤ x ≤ 0.26). With the accumulation of BZT content, relax behaviors were observed by dielectric properties measurements. At the MPB, the crystal structures of the R phase and T phase change abruptly. The distortion degree of the R phase increases, and the differences between a and c of the T phase decrease. An enhanced ferroelectricity Pr of ~27.8 μC/cm2 and apex piezoelectric coefficient d33 of 131 ± 4 pC/N are obtained near the MPB (x = 0.25), due to the R-T phase coexistence near room temperature. The results show that BFS-xBZT ceramics could be a candidate for lead-free piezoelectric ceramics at high operating temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.