Abstract
Due to the merits of high safety and easy preparation, dielectric ceramics have become key engineering materials for capacitors. Within this article, different contents of Na0.5Bi0.5TiO3 were introduced into Ba0.65Sr0.245Bi0.07TiO3 relaxor ferroelectric ceramics in order to increase the disorder degree of A-site ions in perovskite structure and modify the relaxation, which could generate liquid sintering promoting densification, then finally enhancing the dielectric energy store performance of ceramics. The research results show that all the bulk samples prepared through traditional processing route are exhibiting pseudocubic perovskite structure, and their surfaces are with Na0.5Bi0.5TiO3 (NBT)-rich phase formed during densification due to a relatively low sintering temperature of NBT. The relaxation coefficient of BT-SBT-0.01NBT ceramic is 1.8. Because of the existence of liquid phase formation during sintering, the dielectric breakdown strength (BDS) of BT-SBT-0.01NBT ceramic is increased to 230 kV/cm, and the recoverable energy density (Wrec) reached 2.22 J/cm3. The introduction of NBT can hence enhance the relaxation and BDS, finally elevate the energy storage performances.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.