Improved dispersion and physico‐mechanical properties of rubber/silica composites through new silane grafting

Abstract

Abstract3‐Octanoylthio‐1‐propyltriethoxysilane (a new silane) grafted styrene butadiene rubber/ silica composites were prepared in the present work, where grafting weight percentage of the base rubber (0%, 2%, 4%, and 6%) and filler content of the composites (0, 5, 15, 35, and 50 phr) were varied to investigate dispersion of the filler in the rubber. A detailed quantitative study of morphology‐physical property relationship of the composites using dispersion degree parameter was carried out. Pronounced improvement of dispersion was observed with increasing grafting weight percentage of the base rubber. A mechanism of polymer to filler interaction was shown by Fourier transform infrared spectroscopy. The dispersion rate constant from the torque‐time curve increased with the grafting percentage. Bound rubber content and Payne effect measurement indicated improved rubber‐filler interaction for the grafted rubber compound. A relation between low strain modulus of the composites and grafting percentage was proposed. The nanoindentation studies gave further insight into the results. Other physico‐mechanical properties at different grafting weight percentages at particular filler loading (50 phr) and at different filler loadings at a particular grafting weight percentage (4%) were evaluated. The improved mechanical and dynamic mechanical properties with increasing grafting weight percentage are an indication that this methodology could be used in green tire application.