Improved corrosion behavior of nanocrystalline zinc produced by pulse-current electrodeposition

Abstract

Pulse electrodeposition was used to produce nanocrystalline (nc) zinc from zinc chloride electrolyte with polyacrylamide and thiourea as additives. Field emission scanning electron microscopy (FESEM) was used to study the grain size and surface morphology of the deposits and X-ray diffraction was used to examine their preferred orientation. Corrosion behavior of the electrodeposited nc zinc in comparison with electrogalvanized (EG) steel in de-aerated 0.5 N NaOH solution was studied using potentiodynamic polarization and impedance measurements. A scanning electron microscope (SEM) was used to characterize the surface morphology of the EG steel before corrosion testing. Surface morphologies of nc zinc deposits and EG steel were also studied after potentiondynamic polarization by SEM. Nanocrystalline zinc (56 nm) with random orientation was produced. The estimated corrosion rate of nc zinc was found to be about 60% lower than that of EG steel, 90 and 229 μA/cm 2, respectively. The surface morphology of corroded nc zinc was characterized by discrete etch pits, however, uniform corrosion was obtained after potentiodynamic polarization of EG steel. The passive film formed on the nc zinc surface seems to be a dominating factor for the corrosion behavior observed.