Abstract
The characteristics of the high energy product NdFeB magnets obtained by the powder metallurgy route have been improved by appropriate vanadium additions. Specific combinations of V and Co lead to an intrinsic coercive force of about 1350 kA/m (17 kOe) in Dy-free magnets, without any large decrease of remanence. If 1.5-at.% Dy is added, load line down to -B/ mu H=0.5 can be achieved at 180 degrees C without irreversible losses. Corrosion resistance is improved by blocking the selective oxidation of the Nd-rich phase. As a consequence, organic-coated magnets are able to withstand 15 days at 115 degrees C-1.75 bars in a H/sub 2/O saturated atmosphere without any degradation. It is concluded that this set of new properties will enlarge the application fields of Nd-F-B permanent magnets. >
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.