Abstract
Abstract In this paper evaluation of sealed and unsealed thermally sprayed aluminum (TSA) for the protection of 22%Cr duplex stainless steel (DSS) from corrosion in aerated, elevated temperature synthetic seawater is presented. The assessments involved general and pitting corrosion tests, external chloride stress corrosion cracking (SCC), and Hydrogen induced stress cracking (HISC). These tests indicate that DSS samples which would otherwise fail on its own in a few days do not show pitting or fail under chloride SCC and HISC conditions when coated with TSA (with or without a sealant). TSA-coated specimens failed only at very high stresses (>120% proof stress). In general, TSA offered protection to the underlying or exposed steel by cathodically polarizing it and forming a calcareous deposit in synthetic seawater. The morphology of the calcareous deposit was found to be temperature dependent and in general is of duplex nature. The free corrosion rate of TSA in synthetic seawater was measured to be ~5-8 µm/year at ~18°C and ~6-7 µm/year at 80°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.