Importance of Low‐Temperature Melt‐Mixing on the Construction of Stereocomplex Crystallites with Superior Nucleation Efficiency in Asymmetric Poly(l‐lactide)/Poly(d‐lactide) Blends

Abstract

AbstractThe nucleation efficiency (NE) of stereocomplex crystallites (SCs) formed in asymmetric poly(L‐lactide)/poly(D‐lactide) (PLLA/PDLA) blends is generally unsatisfactory because the competition between stereocomplexation and chain mixing involved in the melt‐mixing process can cause low formation efficiency and even severe aggregation of SCs. Herein, it is attempted to achieve high‐efficient formation of finely dispersed SCs particles by designing a unique melt‐mixing procedure, where the mixing of PLLA with 0.75 wt% PDLA is first performed at elevated temperatures (far above the melting temperature of SCs) to allow the homogeneous mixing of PLLA/PDLA chains and then at a low temperature (slightly above that of homocrystallites) to permit the full stereocomplexation of the premixed chains. It is found that the SCs formed in the blends exhibit unexpectedly low NEs (e.g., 54.5%), much inferior to that (73.6%) in the counterpart without undergoing premixing. This is because the introduction of premixing leads to a remarkable deterioration in the amount of SCs particles formed, despite decreased particle size, highlighting that the direct mixing at low temperatures of 170–180 °C (about 20–30 °C lower than that used in common melt‐processing of PLA) is more effective for the construction of SCs with superior NE. The mechanisms for these striking findings are discussed.