Abstract
Utilizing a direct film coating method (DFCM), such as doctor blade coating, offers a promising approach for efficient and scalable catalyst layer (CL) production for fuel cells. To further widen the understanding of lab-scale DFCM, the present research investigates how different Pt-based catalyst ink formulations coated via doctor blade coating with varying blade gap thickness (BGT) affect the CL quality and catalyst loading. In total, 120 CL samples were prepared by coating 20 different catalyst ink formulations with varying solids content, ionomer-to-carbon (I/C) ratio, and water-to-isopropanol solvent ratio with BGTs of 75, 125, and 200 μm. Inspection of these samples showed that the solvent ratio affects the coating uniformity, with the most uniform films achieved with a ratio of 1.67 or greater. Furthermore, increasing the I/C ratio for a given solids content ink formulation decreases the Pt loading, whereas an I/C ratio above or below 1.0 reduces cell performance due to mass transport or proton conductivity impacts, respectively. In addition, a relationship factor and equations are presented to estimate the solid weight and catalyst loading of the fabricated CL based on the ink formulation and BGT. Overall, this work provides important guidance for lab-scale DFCM fabrication of industrially relevant CLs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.