Abstract
Beryllium samples from the JET ITER-like wall limiter tiles with either co-deposits or surface cracks caused by melt damage, were immersed into boiling water for 4 h 15 min to simulate and assess the impact of coolant water ingress into a tokamak on the state of Be components. Microscopy of the water-treated surfaces and the lack of residue in the water revealed that no thermomechanical damage (cracking or exfoliation) occurred to the samples during the exposure. Ion beam analysis showed no measurable release of deuterium from the samples. Combined ion beam analysis and Raman spectroscopy indicated only some degree of surface oxidation, but no thick oxide films were formed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.