Abstract
Optical absorption and luminescence spectra were recorded at different temperatures for the Czochralski grown crystals of Lu2SiO5-Gd2SiO5 solid solution (LGSO) single doped with Er3+ and double-doped with Er3+ and Yb3+. Optical anisotropy and intensities of Er3+ transitions in LGSO were determined from analysis of room temperature polarized absorption spectra. The crystal field splitting of multiplets and linewidths of Er3+ transitions were derived from low-temperature 6 K absorption and luminescence spectra. Spectra of the Er3+ luminescence excited at 380 nm and of up-converted luminescence excited at 803 nm and 975 nm were recorded for samples with different Yb3+ concentration as a function of temperature between 300 K and 775 K. Thermographic parameters of LGSO:0.5%Er,5%Yb sample derived for FIR (2H11/2/4S3/2) are comparable to those observed in other hosts co-doped with Er and Yb ions, corroborating suitability of this system for the purpose of optical thermometry. For all samples studied the relative thermographic sensitivity Sr(max) values for the 4S3/2/4F9/2, 4F7/2/4S3/2 and 4F7/2/4F9/2 pairs are smaller as compared to 2H11/2/4S3/2 pair but they occur at higher temperatures and therefore may be of interest for specific applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.