Abstract
The potential of twin-belt cast (TBC) AlMg1SiCu sheet for structural automotive applications was investigated with a particular emphasis on the impact of pre-ageing on its age hardening response. The optimum T6 process for the TBC AlMg1SiCu sheet is identified to be a water-quench from the solution heat treatment at 540 °C and a subsequent ageing treatment at 180 °C. This process gives hardness values as high as 120 HV within several hours when ageing at 180 °C is performed shortly after the solution treatment. The age hardening capacity is impaired, however, when the sheet is stored at room temperature before the artificial ageing cycle. Pre-ageing at 100 and 140 °C is effective in improving the age hardening response of the naturally aged 6061 sheet. Pre-ageing suppresses natural ageing and clustering activities and gives lower T4 yet a much higher T6 hardness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.