Impact of PEG400–Zeolite Performance as a Material for Enhancing Strength of the Mechanical Properties of LECA/Foamed Lightweight Concrete

Abstract

A versatile building material, foamed concrete is made of cement, fine aggregate, and foam combined with coarse aggregate. This study provides a description of how constant coarse aggregate replacement (50%) of LECA and foamed concrete, which are lightweight concrete types, by zeolite as a filler and PEG-400 as a plasticizer, water retention agent, and strength enhancer affect the mechanical properties of the cement. A study that examined the characteristics of cellular lightweight concrete in both its fresh and hardened forms was carried out for both foamed concrete and LECA concrete. In order to do this, a composite of zeolite and polyethylene glycol 400 was made using the direct absorption method, and no leakage was seen. Zeolite was loaded to a level of 10% and 20% of the total weight in cement, while 400 g/mol PEG was used at levels of 1%, 1.5%, and 2% of the cement’s weight. Various mixtures having a dry density of 1250 kg/m3 were produced. Properties like dry density, splitting tensile strength, and compressive strength were measured. An increase in the amount of PEG400–zeolite was seen to lower the workability, or slump, of both foamed and LECA concrete, while the replacement of aggregate by zeolite resulted in an exponential drop in both compressive and flexural strengths.