Abstract
ABSTRACT These days, green composites are getting a lot of attention for their biodegradability, sustainability, and affordability. This study applies polylactic acid as the matrix and untreated and surface-treated kenaf fibers as reinforcement to fabricate kenaf-reinforced PLA-based composites. Kenaf fibers are exposed to three different chemical treatments (sodium hydroxide, potassium permanganate, and potassium dichromate) and investigate the effect of surface modifications on the mechanical properties of kenaf/PLA composites. The surface modified fibers were characterized by FTIR Spectroscopy. The consequences of processing variables such as fiber volume percent ranging from 25% to 50% and molding temperature range of 160°C to 180°C were also examined on the mechanical characteristics of developed composites and are validated using SEM analysis. Surface modifications result in improved tensile and flexural characteristics of developed treated kenaf/PLA composites. Alkali treated woven kenaf fiber composites with greater matrix adhesion have optimum tensile and flexural strength of 72.81 MPa and 94.45 MPa respectively. The present study revealed that composites (fabricated at 170°C molding temperature) have maximal tensile and flexural strength at 35% fiber volume fraction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.