Gamma or electron beam irradiation of ultra-high molecular weight polyethylene (UHMWPE) used in artificial joints for sterilization and/or crosslinking purposes generates free radicals in the material, which causes long-term oxidative degradation of UHMWPE. Recently, another mechanism for the degradation of UHMWPE by the absorption of lipids during in vivo clinical use was proposed. However, knowledge on lipid-induced degradation is quite limited, compared with that on radical-induced degradation. In this study, lipid-induced degradation was simulated using squalene absorption and subsequent accelerated aging, and its impact on the mechanical properties of UHMWPE was evaluated. The simulated lipid-induced degradation caused an increased elastic modulus and decreased elongation with maximum degradation at the surfaces. These results imply that degradation of UHMWPE may occur during in vivo long-term use, even if free radicals are completely eliminated. Therefore, further investigation is required to clarify the impact of lipid-induced degradation on clinical outcomes, such as the wear and fatigue characteristics of UHMWPE components.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.