The impact of a dopant (X; X = Y or Sc) in zirconia on carbon deposition in CH4 and CH4/H2O environments was studied experimentally and via first-principles calculations. In the CH4 environment, the apparent activation energy for the carbon deposition of Ni/ScSZ was lower than that of Ni/YSZ. SEM/EDS observation indicated the Ni/XSZ interface was key to elucidating the dopant-induced difference. To clarify the difference, the calculation presented two mechanisms: first, the vacancy in ScSZ rather than that in YSZ was readily moved to a neighboring site, thereby stabilizing the vacancy configuration after CH–CH bonding. Second, Ni was readily distorted in Ni/ScSZ at the specific vacancy configuration, thereby decreasing the forward activation energy. In CH4/H2O environment, the calculation showed larger dopant Y caused steric hindrance to prevent CH + O→CHO which was the sensitive reaction in the steam reforming. This explained lower reforming rate in Ni/YSZ than in Ni/ScSZ.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.