Abstract
DC-sputtered Mo back contact layers were deposited on soda-lime glass (SLG) with different power densities applied on the Mo target to study its influence on the photovoltaic performance of Cu(In,Ga)Se2-based (CIGSe) solar cell. CIGSe absorber was then deposited simultaneously on these SLG/Mo, following the 3-stage process. These devices have good but different photovoltaic performance (>16% efficiency without MgF2 coating). To find a material origin, secondary ion mass spectroscopy (SIMS) profiles were carried out on complete cells, revealing that Na and K content and distribution in each layer depend on the deposition conditions of the back contact. Even before the CIGSe deposition and despite similar morphologies, Na content can vary 10-fold from one Mo layer to another. The same applies to the absorber; when grown on a different Mo they present the same grain boundary density but different alkali contents in bulk or at interfaces. This has an influence on the compositional grading in absorber, confirmed by X-ray diffraction and SIMS.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.