Abstract
The impact compressive failure behavior of a unidirectional T700/2521 carbon/epoxy laminated composite in three principal material directions or fiber (1-), in-plane transverse (2-) and through-thickness (3-) directions is investigated on the conventional split Hopkinson pressure bar (SHPB). Cubic and rectangular block specimens with identical square cross section are machined from an about 10 mm thick composite laminate. The uniaxial compressive stress-strain curves up to failure at quasi-static and intermediate strain rates are measured on an Instron testing machine. It is shown that the ultimate compressive strength and strain exhibit no strain-rate effect in the 1-direction, but a slight strain-rate effect in the 2-and 3-direction over a range of strain rates from10-3 to 103/s.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.