Abstract
The aerospace industry uses glass fibre reinforced polymer (GFRP) composites to manufacture structural and non-structural parts of an aircraft as they possess superior strength to weight ratio and exceptional corrosion resistance. Commercial aircraft operate in a very wide temperature ranges from -54 to 55 °C. Potential GFRP laminates are susceptible to impact during aircraft operation, and the temperature at impact governs the nature of damage and failure mechanisms. As a result, the current study focuses on examining how aeronautical GFRP composites behave in various temperature environments that are encountered during high- and low-altitude operations. Using S2-glass fibre/FM94-epoxy unidirectional prepreg, GFRP plates were created. Drop weight impact tests were conducted at ambient (25 °C), high (50, 75, 100 °C), and low (-25, -55 °C) temperatures, as well as at various impact energies (75, 150, 225 J). The damages were assessed visually, along with their sizes. Each testing scenario's impact parameters, including the impact load, deflection, and energy absorption, were also examined. In Abaqus/Explicit, a coupled temperature-displacement numerical model was created to predict the onset of stress and damage. According to experimental findings, GFRP plates are stiffer and show less apparent damage at cryogenic temperatures (∼15-34% lower displacement) than they do at other temperatures. Furthermore, it was observed that the matrix softens at high temperatures, showing larger damaged area at entry but with less obvious damage and increasing energy absorption, while semi-perforation occurred under cryogenic temperatures at entry with smaller damaged area. A strong correlation is shown between the experimental and FE data, confirming the capability of FE models to predict impact damage and deflections at different temperatures in the future.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.