Abstract

Boroaluminosilicate geopolymers were used for the immobilization of heavy metals. Then, their mechanical properties, phase composition, structure, and microstructure were investigated. The addition of borax and boric acid did not induce the formation of any crystalline phases. Boron was incorporated into the geopolymeric network and caused the formation of N–B–A–S–H (hydrated sodium boroaluminosilicate) gel. In the range of a B/Al molar ratio of 0.015–0.075, the compressive strength slightly increased (from 16.1 to 18.7 MPa), while at a ratio of 0.150, the compressive strength decreased (to 12 MPa). Heavy metals (lead and nickel) were added as nitrate salts. The loss of the strength of the geopolymers induced by heavy metals was limited by the presence of boron. However, it caused an increase in heavy metal leaching. Despite this, heavy metals were almost entirely immobilized (with immobilization rates of >99.8% in the case of lead and >99.99% in the case of nickel). The lower immobilization rate of lead was due to the formation of macroscopic crystalline inclusions of PbO·xH2O, which was vulnerable to leaching.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.