Abstract
Abstract A micro-structuring of the tungsten plasma-facing surface can strongly reduce near surface thermal stresses induced by ELM heat fluxes. This approach has been confirmed by numerical simulations with the help of ANSYS software. For experimental tests, two 10 × 10 mm2 samples of micro-structured tungsten were manufactured. These consisted of 2000 and 5000 vertically packed tungsten fibres with dimensions of O240 µm × 2.4 mm and O150 µm × 2.4 mm, respectively. The 1.2 mm bottom parts of the fibres are embedded in a copper matrix. The top parts of the fibres have gaps about of 10 µm so they are not touching each others. The top of all tungsten fibres was electro-polished. A Nd:YAG laser with a pulse duration 1 ms and a pulse repetition frequency of 25 Hz was used to simulate up to 105 ELM-like heat pulses. No damage on either of the micro-structured tungsten samples were observed. Neon plasma erosion rate and fuel retention of the micro-structured tungsten samples were almost identical to bulk tungsten samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.