Abstract
A systematic increase of the average hyperfine magnetic induction at57Fe measured at room temperature during interrupted isothermal annealing was found to be inherent to the irreversible relaxation processes in the Fe−B based soft magnetic alloys at moderately elevated temperatures. Assuming superimposed asymptotic exponential field vs. time dependences. several processes can be distinguished, their relaxation times determined and from the Arrhenius-like log τ vs. 1/T plots average activation enthalpies estimated. Results on the Fe70Co10B20 and Fe85−x Co x B15 (x=17, 19 and 21 at. % Co) amorphous ribbons between 100 and 200°C are compared and discussed in terms of possible stress relief, free volume annihilation and short range ordering mechanisms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.