Abstract
In recent years, porous organic polymers (POPs) have received increasing attention and research interest due to their formidable potential applications in gas storage/separation, heterogeneous catalysis, photoelectricity, energy storage and conversion, etc. In this work, we report the design and synthesis of a hydroxyl-functionalized porous organic polymer (PCz-res) by conventional FeCl3-facilitated oxidative polymerization for gas adsorption and energy storage applications. The precursor Cz-res was designed and synthesized by the imidization of anhydride bearing twisted carbazole units with 4,6-diaminoresorcinol. The prepared PCz-res polymer was completely characterized by the usual analytical techniques. PCz-res exhibited a high specific surface area of 1015 m2/g and reversibly adsorbed 20.53 wt% (273 K) and 14.92. wt% (295 K) CO2 at 1 bar with a moderate isosteric heat of CO2 adsorption (22.39 kJ/mol). The favourable properties of PCz-res were attributed to the uniform pore size distribution (0.8 nm), high surface area, rich nitrogen content and presence of polar CO2-philic hydroxyl groups in the polymeric network. These features make the investigated polymer a plausible emerging material in the field of gas adsorption and separation. Moreover, PCz-res was applied in supercapacitor energy storage and exhibited a specific capacitance as high as 434 F g−1 in 1 M H2SO4 at a 2 mV/s scan rate and 367 F g−1 at a current density of 0.5 A g−1. Additionally, PCz-res retained 91% of the initial specific capacitance after 2000 charge/discharge cycles at a current density of 10 A g−1. The structural characteristics of PCz-res lead to a larger accessible surface area and a redox-active structure, resulting in efficient charge energy storage.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.