Abstract
ObjectivesTo test the demineralization potential, bonding performance, and dentin biostability when using hydroxy acids for etching enamel and dentin. MethodsSurface microhardness, roughness and depth of demineralization were investigated after etching enamel and dentin with 35 % glycolic acid (Gly), tartaric acid (Ta), gluconic acid (Glu), gluconolactone (Gln), or phosphoric acid (Pa) (n = 5/group). Dentin microtensile bond strength (μTBS) after 24 h or 1 year of bonding (n = 8 teeth/group) and enamel shear bond strength (SBS) after 24 h (n = 10 teeth/group) were obtained. In dentin, failure mode was classified as adhesive, cohesive in dentin/resin, or mixed. Dentin biostability was assessed by loss of dry weight and collagen degradation after 30-day incubation (n = 10 beams/group). Statistical analysis consisted of ANOVA with post-hoc Tukey’s HSD, Tukey-Kramer test, Bonferroni correction, and Fisher’s exact tests (α = 0.05). ResultsGly showed better or similar results than Pa for enamel microhardness and dentin roughness, while no significant differences were observed among Ta, Glu, and Gln (p > .05). Hydroxy acids produced significantly shallower demineralization than Pa (p < .05). Gln resulted in the lowest SBS and μTBS, while Gly, Glu, Ta, and Pa showed no significant difference. There was no significant difference in μTBS between 24 h and 1 year of storage. The association between failure mode and etchant was statistically significant after 24 h only (p < .001). Hydroxy acids resulted in higher dentin biostability than Pa (p < .05). ConclusionsGly, Glu and Ta resulted in adequate bonding performance and reduced dentin degradation and are potential alternative etchants to improve long-term stability of adhesive restorations. Clinical significanceThis study supports the potential use of hydroxy acids as alternative etchants when bonding to enamel and dentin and demonstrates that specific acids are more suitable to be used in adhesion since they result in appropriate bond strength and less dentin degradation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.