Abstract
Tetragonal Barium titanate (BaTiO3) nanotube arrays have been prepared using the template-assisted hydrothermal method combined with an annealing process. The in-situ chemical conversion of TiO2 nanotube array templates ensured that BaTiO3 maintained the morphology of the nanotube architectures. Moreover, X-ray diffraction and Raman spectrum characterization were used to confirm that the BaTiO3 nanotube arrays had a tetragonal phase after the use of a simple annealing technique. Typical hysteresis loops showed their ferroelectricity, with the remanent polarization and coercive fields being 2.57 microC/cm2 and 2.52 kV/cm, respectively. The relative dielectric constant of the tetragonal BaTiO3 nanotube arrays reached up to 1000 and the dielectric loss was as low as 0.02 at 1 kHz at room temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.