Hydrothermal synthesis of red phosphorus @reduced graphene oxide nanohybrid with enhanced electrochemical performance as anode material of lithium-ion battery

Abstract

Red phosphorus @reduced graphene oxide (P @rGO) nanohybrid was synthesized via a two-step hydrothermal process. The obtained P @rGO nanohybrid was characterized by TEM, SEM, Raman, XRD and XPS. It was found that the nano-scale red phosphorus encapsulated in the reduced graphene oxide and the existence of phosphorus promote the reduction of graphene oxide. The electrochemical performance of P @rGO nanohybrid as an anode material was investigated by galvanostatic charge/discharge, rate performance, cyclic voltammetry and AC impedance test. With increasing the mass of rGO, the electrochemical performance of P @rGO nanohybrid was significantly enhanced. The first discharge/charge specific capacity of the nanohybrid prepared at optimum condition (P:GO = 7:3) could achieve approximately 2400 mAh/g and 1600 mAh/g respectively and still retained ∼1000 mAh/g after 80 cycles and the coulombic efficiency maintained almost 100%. The enhancement in P @rGO nanohybrid was attributed to the introduction of graphene, which led to the elimination of volume effect and the enhancement of conductively of pure red phosphorus.