Abstract
In this paper, 1D single-crystalline MnO2 nanowires have been successfully synthesized by hydrothermal method using KMnO4 and (NH4)2S2O8 as raw materials. X-ray diffraction patterns and high-resolution TEM images reveal pure tetragonal MnO2 phase with diameters of 15–20 nm. Photoluminescence studies exhibited a strong ultraviolet (UV) emission band at 380 nm, blue emission at 452 nm and an extra weak defect-related green emission at 542 nm. UV–visible spectrophotometery was used to determine the absorption behavior of nanostructured MnO2 and a direct optical band gap of 2.5 eV was acquired by Davis–Mott model. The magnetic properties of the products have been evaluated using vibrating sample magnetometer, which showed that MnO2 nanowires exhibited a superparamagnetic behavior at room temperature. The magnetization versus temperature curve of the as-obtained MnO2 nanowires shows that antiferromagnetic transition temperature is 99 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.