Abstract
Polyethersulphone/sulfonated polysulfone/TiO2 (PES/SPSf/TiO2) ultrafiltration (UF) mixed matrix membranes (MMMs) were coated with a hybrid layer composed of branched polyethyleneimine (PEI) and TiO2 nanoparticles (NPs) crosslinked by glutaraldehyde (GA) to enhance its stability. The effect of TiO2 NPs loadings on the thickness, surface wettability, surface charge and molecular weight cut-off (MWCO) was explored. The corresponding MWCO decreased from 96 kDa for the pristine PES/SPSf/TiO2 MMM (M0) to 8.5 kDa for PEI-GA@MMMs (M1), and then gradually increased to the range of 15 kDa–40 kDa for PEI-TiO2/GA@MMMs. TiO2 NPs having abundant –OH groups also increased electronegativity and hydrophilicity of the composite membranes. At neutral pH, the zeta potential changed from negative charge of MMMs (−33 mV) into positive charge of M1 (1.3 mV), then into negative charge (−7.4 mV) in the optimum hybrid coated membrane PEI-TiO2 (0.025 wt%)/GA@MMMs (M3). The underwater oil contact angle (UWOCA) of with hexane, gasoline, dichloromethane and petroleum ether was 165°, 167°, 164° and 135°, respectively. The air/water contact angle (WCA) of M3 was 42°, which is lower than that of M1 (63°). It is important to note that M3 demonstrated a high rejection of different oil-in-water emulsions with <300 nm oil droplets (>90 %) and an improved pure water permeance of 62 LMH bar−1 compared to 44 LMH bar−1of M1. M3 also exhibited double the antifouling rates of M1 hence corroborating wettability and surface charge results. In summary, our current study provides an available tuning approach to engineering membranes for the treatment of oil-in-water emulsions containing nano-sized oil droplets.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.