Abstract
The hydrolytic degradation of a series of poly-L-lactide (PLLA)-polyisobutylene (PIB) multiblock copolymers was studied in phosphate buffer solution (pH = 7.4) at 37 °C. The multiblock copolymers were synthesized by chain extension of PLLA-b-PIB-b-PLLA triblock copolymers, which were obtained by ring-opening polymerization of L-lactide initiated by hydroxyallyl telechelic PIB. The degradation strongly depended on the PLLA segment length. At constant PIB segment length, the multiblock copolymer with the shortest PLLA segment length (DPn = 10), showed significant weight loss after 8 weeks, whereas weight loss for DPn = 36 was only observed after 24 weeks. The gel-permeation chromatographic analysis showed a similar decrease in the number-average molecular weight (M n ) with time further supporting the weight loss data. Dynamic mechanical analysis showed a decrease in ultimate stress and modulus with time. The crystallinity of multiblock copolymers changed significantly with degradation time as indicated from differential scanning calorimetric analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part A: Polymer Chemistry
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.