Hydrogenation of cyclohexene over single-atom Pt or Pd incorporated porous ceria nanoparticles under solvent-free conditions.

Abstract

In order to maximize the utilization of noble metals in catalysis, single atom of palladium (Pd) and platinum (Pt) were incorporated individually in the framework of porous ceria (CeO2) by using a one-step flash combustion method. Samples with different Pd and Pt loading (0.5, 1, 2.5, and 5 wt%) were prepared and examined by using different analysis techniques such as XRD, ICP, N2 sorption measurements, SEM, HR-TEM, and XPS. The characterization data confirms the formation of zero-state single-atom Pt and Pd (with possible formation of Pd nanoparticles with a size less than 5 nm) incorporated onto the three-dimensional porous ceria structure. The catalytic activity of the synthesized materials was studied in the cyclohexene reduction to cyclohexane at 393 K and 3 atm of pure hydrogen (H2) gas as a model reaction. The obtained results demonstrated that the conversion percentage of cyclohexene is increasing with Pd or Pt loading. The best cyclohexene conversion, 21% and 29%, was achieved over the sample that contains 5 wt% of Pt and Pd, respectively. The collected catalytic data fit the zero-order reaction model, and the rate constant of each catalyst was determined. The catalytic experiments of the most-performed catalysts were repeated five times and the obtained loss in activity was insignificant.