Abstract
Abstract A series of 50 wt% Mn 2 O 3 sorbents was prepared using various mesoporous silica, MCM-41, HMS, and KIT-1 as support. The influence of textural parameters of mesoporous silica, especially type of channel on the desulfurization performance of Mn 2 O 3 sorbents was investigated at 600–850 °C using hot coal gas containing 0.33 vol.% H 2 S. The fresh and used sorbents were characterized by means of N 2 -adsorption, x-ray diffraction (XRD), high resolution transmission microscopy (HRTEM) and H 2 temperature- programmed reduction (H 2 -TPR) techniques. The results confirmed that the manganese oxide was dispersed highly in regular pore channel of the mesoporous supports due to high surface area. Compared with the Mn 2 O 3 /diatomite, all mesoporous silica supported Mn 2 O 3 sorbents exhibited high breakthrough sulfur capacity and a sharp deactivation rate after the breakthrough point. Compared to Mn 2 O 3 /MCM-41 and Mn 2 O 3 /HMS sorbent, the Mn 2 O 3 /KIT-1 showed better desulfurization performance because of the 3D wormhole-like channel. The high sulfur capacity of the Mn 2 O 3 /KIT-1 sorbent was maintained during the eight consecutive desulfurization-regeneration cycles. The Mn 2 O 3 /KIT-1 still presented high desulfurization activity when hot coal gas contained low steam (
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call