Abstract
To understand the influence of various crystallographic phases on hydrogen storage properties, ball milling of MgH 2 with hexagonal (α) and cubic (β) SiC have been performed. Structural characterization of all samples has been done by X-ray diffraction (XRD) analysis, particle size analysis and scanning electron microscopy (SEM). Investigation of hydrogen desorption properties of prepared nanocomposites has been done using temperature programmed desorption (TPD) technique. Despite the results of structural and morphological characterization of obtained nanocomposites are very similar, TPD spectra show significant differences regarding existence of intermediate temperature peak. In the sample milled with hexagonal SiC this peak originates both from H 2 and H 2O, while in the sample milled with cubic phase it only comes from H 2O. Both samples exhibit low temperature H 2 peak at 385 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.