Abstract
Samples of single wall carbon nanotubes (SWNTs) were prepared using a solar reactor. Graphite targets containing different catalysts (Ni/Co, Ni/Y, Ni/Ce) allowed the synthesis of SWNTs soot in which nanotubes had different diameter distributions. Several consecutive stages of HCl treatment and thermal oxidation in air (HCl protocol) purified the samples. Another protocol involving HNO 3 treatment and H 2O 2 oxidation (HNO 3 protocol) was also used. Isotherms of hydrogen adsorption were volumetrically measured at 253 K under pressures below 6 MPa on raw and treated samples. The highest adsorption capacity (0.7 wt%) was measured on raw soot. HCl protocol clearly increases the BET surface area ( S BET ) and the microporous volume ( W 0 ( N 2 ) ) measured by N 2 at 77 K of the treated samples with respect to the as-produced materials, whereas HNO 3 protocol decreases them. A correlation between textural properties and hydrogen storage capacities is discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.