Abstract
A thermodynamic assessment of hydrogen sorption in LaNi5-xAlx-H (0 ≤ x ≤ 1) alloys was performed combining experimental and theoretical investigations. The occurrence of sloped plateaux in Pressure Composition Isotherms (PCI) is discussed on the basis of compositional inhomogeneities and of possible re-distribution of metallic elements between the hydrogen rich and the hydrogen poor phases.In order to provide input for the thermodynamic assessment, literature data were reviewed and PCI experiments were performed at increasing temperatures on alloys with different Al contents. The presence of a compositional distribution was investigated using Rietveld refinement of X-Ray diffraction patterns, volumetric and calorimetric measurements, both on as received and annealed samples with LaNi4.8Al0.2 nominal composition. Moreover, ab initio energies of formation for LaNi5, LaAl5 and the respective hydrides were calculated. A full CALPHAD assessment of the Gibbs energy for LaNi5-xAlxHy (0 ≤ x ≤ 1, 0 ≤ y ≤ 7) phase was obtained, showing a good agreement between experimental and calculated results.The presence of sloped and flat plateaux has been related to the occurrence of ortho- and para-equilibrium conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.