Abstract
The characteristics and hydrogen reduction behavior of W-0.8 wt% Ni-0.4 wt% Cu powder synthesized from WO3-NiOCuO composite powder have been investigated. The metal oxide powder mixtures were prepared using a ball milling process. XRD analysis and HR-TEM revealed that the oxide powders are changed to W and CuNi alloy powders with an average particle size of about 100 nm by hydrogen reduction. To understand the reduction behavior of oxide powders, TG analysis was performed, and the reduction kinetics was evaluated by the amount of peak shift with heating rates. The activation energies for the reduction of WO3-NiO-CuO, estimated by the slope of the Kissinger plot, were measured as 60.6-114.4 kJ/mol depending on reduction steps.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.