A ternary Ni–BaCe0.9Y0.1O3 (BCY)–Ce0.9Gd0.1O2 (GDC) cermet involving 40 vol% Ni was fabricated, and its hydrogen permeation characteristics were evaluated when the GDC volume fraction was varied from 0 to 30 vol%. The X-ray diffraction results of the cermet after sintering at 1400 °C revealed that GDC was dissolved in BCY when the GDC volume composition was 20 vol%. Regardless of the BCY and GDC volume fractions, the metal conductivity of the cermet was dominated by Ni. After the addition of only 1 vol% GDC, the particle sizes of Ni and BCY in the cermet significantly decreased, and the particle size decreased as the volume fraction of GDC increased. The hydrogen permeability increased with increasing temperature and for up to 10 vol% GDC, and a maximum permeation rate of 0.142 mL min−1 cm−2 was obtained at 700 °C. This value is comparable to or better than previously reported values for Ni-cermets under the same conditions. The amount of hydrogen permeation decreased above 10 vol% GDC. This study demonstrated that Ni-BCY-GDC cermet is a material that has both high hydrogen permeability and CO2 resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.