Abstract
The influence of co-existing gases on the hydrogen permeation was studied through a Pd-coated V89.8Cr10Y0.2 alloy membrane. Preliminary hydrogen permeation experiments have been confirmed that hydrogen flux was 6.26 ml/min/cm2 for a Pd-coated V89.8Cr10Y0.2 alloy membrane (thick: 0.5 mm) using pure hydrogen as feed gas. Also, the hydrogen permeation flux decreased with decrease of hydrogen partial pressure at constant pressure when H2/CO2 and H2/CO2/H2S mixture applied as feed gas respectively and permeation fluxes were satisfied with Sievert's law in different feed conditions. It was found from XRD and SEM results after permeation test that the Pd-coated V89.8Cr10Y0.2 alloy membrane had good stability and durability for various mixture feeding conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.