Abstract
Properties of physical vapor deposited diamondlike carbon (DLC) films and the migration of hydrogen in H+ and He+4 ion implanted and hydrogen co-deposited DLC films have been studied. Measurements utilizing Rutherford backscattering spectrometry showed that the films studied have an average mass density of 2.6±0.1 g/cm3. The bonding ratio sp3/sp2 is typically 70% measured with the electron spectroscopy for chemical analysis technique. Impurities and their depth distributions were deduced from the particle induced x-ray emission and secondary ion mass spectrometry (SIMS) measurements. Distributions of implanted and co-deposited hydrogen were measured by the nuclear resonance reaction H1(15N,αγ)12C and SIMS. It was found that annealing behavior of implanted H in DLC has a diffusion like character. The obtained diffusion coefficients resulted in the activation energy of 2.0±0.1 eV. It was observed that in H co-deposited DLC films the temperature of H release varied between 950 and 1070 °C depending on the H concentration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.