The present work considers the effect of hydrogen on the mechanical properties of generic Fe-C-W alloys. Thermal treatment aimed at a martensitic microstructure and two conditions are compared; i.e. an as-quenched state and a quenched and tempered state with lower dislocation density and with W based carbides formed during tempering. The hydrogen induced mechanical degradation is evaluated by in-situ tensile tests, while thermal desorption spectroscopy, hot/melt extraction and permeation experiments are performed to understand the observed hydrogen embrittlement degree. The hydrogen induced ductility loss increases with increasing carbon content due to the higher amount of hydrogen trapped by the denser martensitic lath boundaries. Furthermore, the quenched and tempered condition shows a lower susceptibility to hydrogen. This is correlated to the reduced hydrogen content when tempered due to a decreased dislocation density and the fact that the tempered induced W2C particles did not trap hydrogen. Moreover, corresponding observations to this interpretation are perceived by permeation experiments since, on the one hand, the diffusion coefficient decreases with carbon content due to the increasing trapping ability of alloy A➔B➔C, and, on the other hand, the diffusivity increases when tempering is applied, which is also linked to the decrease in dislocation density and the disability of the carbides to hinder hydrogen diffusion by efficient trapping.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.